Атрибути на продукта

Модел №: EN10025-6

Марка: Houming

Standard: Bs, Din

Place Of Origin: China

Species: Steel Plate

Production Process: Hot Rolled

Surface Treatment: Coated, Galvanized

Приложение: Container Plate, Flange Plate, Ship Plate

Special Steel: High-Strength Steel Plate

Tolerance: ±1%

Category: Ship Steel Plate, Hot Rolled Steel Sheet, Steel Plate, Low-Alloy Plate, Hot-Galvanized Steel Sheet

Processing Service: Bending, Welding, Decoiling, Cutting, Punching, Bending Welding

Възможност за доставк...

транспорт: Ocean,Land

Място на произход: Китай

порт: qingdao,tianjin,shanghai

Вид плащане: L/C,T/T,D/P,D/A

Инкотерм: FOB,CFR,CIF,EXW

Опаковка & доставка

Продажба на единици:

Metric Ton

Висококачествена 10025-6 ниска сплав с висока якота стоманена плоча

EN10025-6 S460Q ниска сплав с висока якост

EN10025-6 S460Q
Chemical composition % MAX
C	Si	Mn	P	S	B	Cr	Cu	Mo	Nb	Ni	Ti
0.22	0.86	1.8	0.03	0.017	0.006	1.6	0.55	0.74	0.07	2.1	0.07
Mechanical properties MIN
	Yield strength (Mpa)			Tensile strength (Mpa)			Elongation %
TH (mm)	＞3≤50	＞50≤100	＞100≤150	＞3≤50	＞50≤100	＞100≤150	17
	460	440	400	550-720		500-670	17

EN10025 -6 S460QL1 горещо валцова стоманена плоча

EN10025 -6 S460QL1
Chemical composition % MAX
C	Si	Mn	P	S	B	Cr	Cu	Mo	Nb	Ni	Ti
0.22	0.86	1.8	0.03	0.017	0.006	1.6	0.55	0.74	0.07	2.1	0.07
Mechanical properties MIN
	Yield strength (Mpa)			Tensile strength (Mpa)			Elongation %
TH (mm)	＞3≤50	＞50≤100	＞100≤150	＞3≤50	＞50≤100	＞100≤150	17
	460	440	400	550-720		500-670	17

EN10025-6 S460QL стоманена плоча

EN10025-6 S460QL
Chemical composition % MAX
C	Si	Mn	P	S	B	Cr	Cu	Mo	Nb	Ni	Ti
0.22	0.86	1.8	0.03	0.017	0.006	1.6	0.55	0.74	0.07	2.1	0.07
Mechanical properties MIN
	Yield strength (Mpa)			Tensile strength (Mpa)			Elongation %
TH (mm)	＞3≤50	＞50≤100	＞100≤150	＞3≤50	＞50≤100	＞100≤150	17
	460	440	400	550-720		500-670	17

EN10025-6 S500QL стоманен лист

EN10025-6 S500QL
Chemical composition % MAX
C	Si	Mn	P	S	B	Cr	Cu	Mo	Nb	Ni	Ti
0.22	0.86	1.8	0.03	0.017	0.006	1.6	0.55	0.74	0.07	2.1	0.07
Mechanical properties MIN
	Yield strength (Mpa)			Tensile strength (Mpa)			Elongation %
TH MM	＞3≤50	＞50≤100	＞100≤150	＞3≤50	＞50≤100	＞100≤150	17
	500	480	440	590-770		540-720	17

EN10025-6 S500Q Стомана с ниска сплав

EN10025-6 S500Q
Chemical composition % MAX
C	Si	Mn	P	S	B	Cr	Cu	Mo	Nb	Ni	Ti
0.22	0.86	1.8	0.03	0.017	0.006	1.6	0.55	0.74	0.07	2.1	0.07
Mechanical properties MIN
	Yield strength (Mpa)			Tensile strength (Mpa)			Elongation %
TH (mm)	＞3≤50	＞50≤100	＞100≤150	＞3≤50	＞50≤100	＞100≤150	17
	500	480	440	590-770		540-720	17

EN10025-6 S550Q стоманен лист

EN10025-6 S550Q
Chemical composition % MAX
C	Si	Mn	P	S	B	Cr	Cu	Mo	Nb	Ni	Ti
0.22	0.86	1.8	0.03	0.017	0.006	1.6	0.55	0.74	0.07	2.1	0.07
Mechanical properties MIN
	Yield strength (Mpa)			Tensile strength (Mpa)			Elongation %
TH (mm)	＞3≤50	＞50≤100	＞100≤150	＞3≤50	＞50≤100	＞100≤150	16
	550	530	490	640-820		590-770	16

EN10025-6 S500QL1 Стоманен лист с ниска сплав

EN10025-6 S500QL1
Chemical composition % MAX
C	Si	Mn	P	S	B	Cr	Cu	Mo	Nb	Ni	Ti
0.22	0.86	1.8	0.03	0.017	0.006	1.6	0.55	0.74	0.07	2.1	0.07
Mechanical properties MIN
	Yield strength (Mpa)			Tensile strength (Mpa)			Elongation %
TH (mm)	＞3≤50	＞50≤100	＞100≤150	＞3≤50	＞50≤100	＞100≤150	17
	500	480	440	590-770		540-720	17

EN10025-6 S500QL1

EN10025-6 S550QL
Chemical composition % MAX
C	Si	Mn	P	S	B	Cr	Cu	Mo	Nb	Ni	Ti
0.22	0.86	1.8	0.03	0.017	0.006	1.6	0.55	0.74	0.07	2.1	0.07
Mechanical properties MIN
	Yield strength (Mpa)			Tensile strength (Mpa)			Elongation %
TH (mm)	＞3≤50	＞50≤100	＞100≤150	＞3≤50	＞50≤100	＞100≤150	16
	550	530	490	640-820		590-770	16

EN10025-6 S620Q

EN10025-6 S620Q
Chemical composition % MAX
C	Si	Mn	P	S	B	Cr	Cu	Mo	Nb	Ni	Ti
0.22	0.86	1.8	0.03	0.017	0.006	1.6	0.55	0.74	0.07	2.1	0.07
Mechanical properties MIN
	Yield strength (Mpa)			Tensile strength (Mpa)			Elongation %
TH (mm)	＞3≤50	＞50≤100	＞100≤150	＞3≤50	＞50≤100	＞100≤150	15
	620	580	560	700-890		650-830	15

EN10025-6 S620QL

EN10025-6 S620QL
Chemical composition % MAX
C	Si	Mn	P	S	B	Cr	Cu	Mo	Nb	Ni	Ti
0.22	0.86	1.8	0.03	0.017	0.006	1.6	0.55	0.74	0.07	2.1	0.07
Mechanical properties MIN
	Yield strength (Mpa)			Tensile strength (MPa)			Elongation %
TH (mm)	＞3≤50	＞50≤100	＞100≤150	＞3≤50	＞50≤100	＞100≤150	15
	620	580	560	700-890		650-830	15

EN10025-6 S620QL1

EN10025-6 S620QL1
Chemical composition % MAX
C	Si	Mn	P	S	B	Cr	Cu	Mo	Nb	Ni	Ti
0.22	0.86	1.8	0.03	0.017	0.006	1.6	0.55	0.74	0.07	2.1	0.07
Mechanical properties MIN
	Yield strength (Mpa)			Tensile strength (Mpa)			Elongation %
TH (mm)	＞3≤50	＞50≤100	＞100≤150	＞3≤50	＞50≤100	＞100≤150	15
	620	580	560	700-890		650-830	15

EN10025-6 S690Q

EN10025-6 S690Q
Chemical composition % MAX
C	Si	Mn	P	S	B	Cr	Cu	Mo	Nb	Ni	Ti
0.22	0.86	1.8	0.03	0.017	0.006	1.6	0.55	0.74	0.07	2.1	0.07
Mechanical properties MIN
	Yield strength (Mpa)			Tensile strength (Mpa)			Elongation %
TH (mm)	＞3≤50	＞50≤100	＞100≤150	＞3≤50	＞50≤100	＞100≤150	14
	690	650	630	770-940		710-900

EN10025-6 S690QL

EN10025-6 S690QL
Chemical composition % MAX
C	Si	Mn	P	S	B	Cr	Cu	Mo	Nb	Ni	Ti
0.22	0.86	1.8	0.03	0.017	0.006	1.6	0.55	0.74	0.07	2.1	0.07
Mechanical properties MIN
	Yield strength (Mpa)			Tensile strength (Mpa)			Elongation %
TH (mm)	＞3≤50	＞50≤100	＞100≤150	＞3≤50	＞50≤100	＞100≤150	14
	690	650	630	760-940		710-900	14

EN10025-6 S690QL1

EN10025-6 S690QL1
Chemical composition % MAX
C	Si	Mn	P	S	B	Cr	Cu	Mo	Nb	Ni	Ti
0.22	0.86	1.8	0.03	0.017	0.006	1.6	0.55	0.74	0.007	2.1	0.07
Mechanical properties MIN
	Yield strength (Mpa)			Tensile strength (Mpa)			Elongation %
TH (mm)	＞3≤50	＞50≤100	＞100≤150	＞3≤50	＞50≤100	＞100≤150	14
	690	650	630	760-940		710-900	14

EN10025-6 S890Q

EN10025-6 S890Q
Chemical composition % MAX
C	Si	Mn	P	S	B	Cr	Cu	Mo	Nb	Ni	Ti
0.22	0.86	1.8	0.03	0.017	0.006	1.6	0.55	0.74	0.07	2.1	0.07
Mechanical properties MIN
	Yield strength (Mpa)			Tensile strength (Mpa)			Elongation %
TH (mm)	＞3≤50	＞50≤100	＞100≤150	＞3≤50	＞50≤100	＞100≤150	11
	890	830	-	940-1100		-	11

EN10025-6 S890QL

EN10025-6 S890QL
Chemical composition % MAX
C	Si	Mn	P	S	B	Cr	Cu	Mo	Nb	Ni	Ti
0.22	0.86	1.8	0.03	0.017	0.006	1.6	0.55	0.74	0.07	2.1	0.07
Mechanical properties MIN
	Yield strength (Mpa)			Tensile strength (Mpa)			Elongation %
TH (mm)	＞3≤50	＞50≤100	＞100≤150	＞3≤50	＞50≤100	＞100≤150	11
	890	830	-	940-1100		-	11

EN10025-6 S890QL1

EN10025-6 S890QL1
Chemical composition % MAX
C	Si	Mn	P	S	B	Cr	Cu	Mo	Nb	Ni	Ti
0.22	0.86	1.8	0.03	0.017	0.006	1.6	0.55	0.74	0.07	2.1	0.07
Mechanical properties MIN
	Yield strength (Mpa)			Tensile strength (Mpa)			Elongation %
	＞3≤50	＞50≤100	＞100≤150	＞3≤50	＞50≤100	＞100≤150	11
	890	830	-	880-1100		-	11

EN10025-6 S960Q

EN10025-6 S960Q
Chemical composition % MAX
C	Si	Mn	P	S	B	Cr	Cu	Mo	Nb	Ni	Ti
0.22	0.86	1.8	0.03	0.017	0.006	1.6	0.55	0.74	0.07	2.1	0.07
Mechanical properties MIN
	Yield strength (Mpa)			Tensile strength (Mpa)			Elongation %
TH (mm)	＞3≤50	＞50≤100	＞100≤150	＞3≤50	＞50≤100	＞100≤150	10
	960	-	-	980-1150		-	10

EN10025-6 S960QL

EN10025-6 S960QL
Chemical composition % MAX
C	Si	Mn	P	S	B	Cr	Cu	Mo	Nb	Ni	Ti
0.22	0.86	1.8	0.03	0.017	0.006	1.6	0.55
Mechanical properties MIN
	Yield strength (Mpa)			Tensile strength (Mpa)			Elongation %
TH （mm）	＞3≤50	＞50≤100	＞100≤150	＞3≤50	＞50≤100	＞100≤150	10
	960	-	-	980-1150		-	10

Когато във фабриката се произвеждат стоманени плочи с нисък сплав, те ще претърпят различни тестове за производителност и ще бъдат тествани многократно, за да се гарантира, че няма разлики в производителността, за да се гарантира, че те отговарят на необходимите стандарти и са подходящи за предназначението им.

Горещо валцувана стоманена плоча

1. Тест за опън

Целта на многократно тестване на опън на стоманена плоча е да се определи якостта на опън, якостта на добив и удължаването на стоманената плоча.

Първата стъпка изисква отрязване на малко парче от стоманената плоча като проба, която е подложена на едноосно напрежение, докато не се счупи; Кривата на напрежението на напрежението се записва, за да се определят свойствата на опън.

2. Основни измервания:

（1） Якост на опън на стоманената плоча: Максималното напрежение, което материалът може да издържи при разтягане или издърпване;

（2） Сила на добив: напрежението, при което материал започва да се деформира пластично.

（3） Удължение: Процентното увеличение на дължината преди счупване, което показва пластичност.

Висококачествена 10025-6 ниска сплав Висока якост